Epro - System Iii Mb

epro • System III MB Moisture / Gas Barrier

Patent Pending

Excellent Strength and Durability • Exceptional Chemical Resistance • Seamless System • Fully Bonded to Slab • Redundant Protection

System Description System III MB is a field installed composite waterproofing and gas vapor barrier that is comprised of a water-based polymer modified asphalt (PMA) membrane sandwiched between two HDPE and polypropylene fabric laminate sheets which provides the durability and chemical resistance of HDPE with the constructability and installation efficiencies of a PMA. (See below for special designs for water table conditions.) System Components

Additional Information

Seamless System – The fluid applied component makes the transition details and field barrier a monolithic installation. Fully Bonded to Slab – The geo-textile surface of the barrier mechanically interlocks with the concrete slab to form a permanent bond between the barrier and slab. Redundant Protection – Multiple waterproofing and gas vapor barriers as well as protection courses. W

OR

LD

OF DIFFE RE N CE

Specifications – Reference “Specification Beneath Slab Moisture Barrier” Detail Drawings – Reference all “MB” labeled Details Installation Guidelines – Reference “Moisture Barrier Installation” and “Repair Procedures – Moisture Barrier” Product Information –Reference “Ecoline-S”, “EcolineR”, “Ecoshield-P”, "Beneath Slab Gas Vapor Barrier" product brochures

Exceptional Chemical Resistance – The HDPE films are very resistant to most contaminates including VOCs.

TI

EA

R

800-882-1896 • rev. sys3-mb_042111

R

W a te r p r oo f i n g Sys tems

ON

FO

S

System Components (Water Table Design) Ecoshield-PB -(Replaces Ecoshield-PP) - A geocomposite membrane comprised of polypropylene fabric and bentonite granules laminated to an HDPE sheet to provide self sealing characteristics and puncture resistance.

Excellent Strength and Durability – The result of the unique field installed composite design.

A

Ecoshield-P (Base Course) – An HDPE film laminated with a nonwoven polypropylene fabric geo-membrane. Ecoline-S (Middle Course) – A spray or fluid applied, water based polymer modified asphalt membrane. Ecoshield-PP (Top Course) – Same as Ecoshield-P except with micro-perforations.

LW ND ORLD CO

I

www.eproserv.com

epro • System III MB - Moisture / Gas Barrier Epro Below Slab Water / Gas Barrier Composite System Testing Composition HDPE film and polypropylene fabric laminate and polymer modified asphalt and HDPE film and polypropylene fabric laminate. ( Ecoshield-P / Ecoline-S / Ecoshield-PP )

Soil Burial* ................................... ASTM D-4068 Weight change ..................... See Note 1 ........ 1.2% ......... passed Tensile Strength ................... See Note 1 ........ 9.89% ....... passed Elongation ............................ See Note 1 ........ 2.2% ......... passed Heat Aging* ................................. ASTM D-4068 Tensile Strength .................. See Note 1 ....... 8.6% ......... passed Elongation .......................... See Note 1 ....... 8.9% ......... passed Environmental Stress Cracking* .. ASTM D-1693 Failure ................................ See Note 2 ........ 620 hrs. .... passed Oil Resistance* .......................... ASTM D-543 & ASTM D-412 Weight change ............................ See Note 1 ....... 7.6% ......... passed Tensile Strength ................. See Note 1 ....... 1.1% ......... passed Elongation .......................... See Note 1 ....... 4.4% ......... passed Methane Transmission* .............. ASTM D-1434 See Note 3 ....... 3.70xE-15.. passed

Chemical Permeation** .... ASTM F-739

Perm Rate Perm Rate Ug/cm2 ml/day

Chlorinated Solvent Perchloroethylene ................................... 69.4 .......... 0.0008 Trichloroethylene ........ ............................ 89.8 .......... 0.0012 Aromatic Hydrocarbon Benzene .................... ............................ 59.3 .......... 0.0013 Chemical Resistance** ...... ASTM D-543 Net change Chlorinated Solvents .. ASTM D-882 Mod. (Less 10% pass) Perchloroethylene Weight ........................ ............................. 4.1% Tensile Strength ......... ............................. 6.5% Tricholorethylene Weight ........................ ............................. 5.4% Tensile Strength ......... ............................. 6.0% Aromatic Hydrocarbon Benzene Weight ........................ ............................. 4.1% Tensile Strength ......... ............................. 4.4% Gases Hydrogen Sulfide Weight ........................ ............................. 0.6% Tensile Strength ......... ............................. 0.8%

OR

LD

OF DIFFE RE N

A

W

CE

* Tests performed by SGS / US Testing ** Tests performed by TRI Environmental *** Tests performed by Momentum Technologies

TI

EA

R

800-882-1896 •

R

Wa te r p r oo f i n g Sys tems

Note 1: LA requires less than 10% Note 2: LA requires over 500 hrs. Note 3: LA requires less than 3 ml per day

ON

FO

S

Tensile Strength* ......................... ASTM D-412 ..... 662 psi Elongation* .................................. ASTM D-412 ..... 45% Adhesion to Concrete*** .............. ASTM C-836 .... 27 lbf/in Puncture Resistance .................... ASTM D-1709 ... 310.9 lbs Hydrostatic Pressure ................... ASTM D-5385 ... 369.5 ft.

LW

O RL D C O

ND

I

www.eproserv.com

rev.sys3mb_042111