20601 OFF WHITE (RAL 9003) • • • • •
Is a high solids two component acrylic coating. It can be applied undiluted or it can be thinned up to 10%, it has good flow and non-sag properties. It hardens rapidly to give a high build, U.V. resistant coating with excellent hiding power, gloss and long term durability. Can be air-dried, low baked or I.R. cured. Is easy to polish once cured.
Preparation of the surface; Cured paint:
1. Wet flat P800-1000 or Dry flat P600-800. 2. Clean off sanding residues. 3. Degrease. 4. Clean with tack rag.
Mixing Ratio 20601:2030
S20600:2030 2:1 1.4-1.8 15-17 4 2-3 40-50 5-10 60 12-14 30 15 4-6
Spray Tip Viscosity DIN 4/sec. Air Pressure/Bar Coats Build/microns. Flash Off/min. Tack Free/min. Through Dry Air/hours Through Dry 60ºC/min. Through Dry I.R./min. Pot-Life /hours
Temperature Range for Use of System 20 2030 Series Hardeners
Temp ºC Hardener 2031 2030 2032 2033
-5
0
5
10
15
20
25
30
35
40
+45
U-POL, 1 TOTTERIDGE LANE, WHETSTONE, LONDON, N20 OEY, UK T: +44 (0)20 8492 5900; F:+44(0)20 8492 5999; E:[email protected]; W: WWW.U-POL.COM
Is a high solids two component acrylic coating. It can be applied undiluted or it can be thinned up to 10%, it has good flow and non-sag properties. It hardens rapidly to give a high build, U.V. resistant coating with excellent hiding power, gloss and long term durability. Can be air-dried, low baked or I.R. cured. Is easy to polish once cured.
Preparation of the surface; Cured paint:
1. Wet flat P800-1000 or Dry flat P600-800. 2. Clean off sanding residues. 3. Degrease. 4. Clean with tack rag.
Mixing Ratio 20601:2030
S20600:2030 2:1 1.4-1.8 15-17 4 2-3 40-50 5-10 60 12-14 30 15 4-6
Spray Tip Viscosity DIN 4/sec. Air Pressure/Bar Coats Build/microns. Flash Off/min. Tack Free/min. Through Dry Air/hours Through Dry 60ºC/min. Through Dry I.R./min. Pot-Life /hours
Temperature Range for Use of System 20 2030 Series Hardeners
Temp ºC Hardener 2031 2030 2032 2033
-5
0
5
10
15
20
25
30
35
40
+45
U-POL, 1 TOTTERIDGE LANE, WHETSTONE, LONDON, N20 OEY, UK T: +44 (0)20 8492 5900; F:+44(0)20 8492 5999; E:[email protected]; W: WWW.U-POL.COM
Related Documents
Ral 9003
May 2020 20
Ra 9003
April 2020 15
La Console Dellelea 9003
October 2019 15
Ral-85p-signed
April 2020 11
Asi-ral-tema-1
October 2019 17