Phenolic - PF Phenol Formaldehyde Foam Advantages Very low density, linear expansion and high oxygen index compared with other phenolics. Disadvantages Very low tensile strength, flexural modulus, heat distortion temperature and low maximum operating temperature compared with other phenolics. Typical Properties
Featured Courses Advanced Materials Masters Course
Property
Value
Density (g/cm 3) Surface Hardness Tensile Strength (MPa) Flexural Modulus (GPa) Notched Izod (kJ/m x 10 .0) Linear Expansion (/°C)
0.08 SD50 0.43 0.02 02 E-5 1.1 0.2 N/A 120 15 40 V0 6
Elongation at Break (%) Strain at Yield (%) Max. Operating Temp. (°C) Water Absorption (%) Oxygen Index (%) Flammability UL94 Volume Resistivity (log ohm.cm) Dielectric Strength (MV/m) Dissipation Factor1kHz Dielectric Constant 1kHz HDT @ 0.45 MPa (°C) HDT @ 1.80 MPa (°C) Material Drying hrs @ °C Melting Temp. Range (°C) Mould Shrinkage (%) Mould Temp. Range (°C)
7 0.001 2.8 2090 NA NA NA NA
Microsystems and Applications Nanotechnology Thermal insulation. Masters Materials Science and Engineering
Source : Abstracted from Plascams For more information on Plascams please visit The Rubber and Plastics Research Association
top
Other AZoNetwork Sites | AZoNano.com | AZoBuild.com | AZoMed.com | Partners - Eng-Tips.com AZoM™ - The A to Z of Materials and AZojomo - The "AZo Journal of Materials Online"...AZoM™.com Pty.Ltd Copyright © 2000-2006
HOME >
TERMS >
ABOUT >
HELPS/FAQS >
MATERIALS >
APPLICATIONS >
INDUSTRIES >
NEWS >
CLASSIFIEDS >
COURSES >
EVENTS >
BOOKS >
JOBS >
JOURNAL >
NEWSLETTER >
ASSOCIATES >